Grain Direction Aluminum Sheet

Two rollers compressing the hot metal cause the polycrystalline material to elongate in the direction of rolling.

Grain direction aluminum sheet. You can define a grain direction to use when calculating the bounding box for sheet metal parts. From the flat pattern properties we can select a new edge for the grain direction. The grain direction is established during the metal rolling process. Bending metal against the grain or perpendicular to the grain is a common way to prevent material failure or cracking.

As a general rule the grain line must run perpendicular to the bend to avoid the potential for cracking or fracture. Bending with the grain or parallel to the grain direction can be a contributor to material failure as bending along the grain allows for separation of the grain boundaries. The three orientations are. You ll now see that your flat pattern is generated based on one edge oriented parallel to the angled edge and the other obviously perpendicular to that in drawing the rectangle.

Whereas bending parallel to rolling direction can lead to cracks because of destruction in grain structure. When working with aluminum plate for example you need to pay close attention to whether you are forming with longitudinal or across transverse the grain direction. You must pay careful attention to grain or rolling direction when bending high strength metals especially when trying to achieve a small inside bend radius. Aluminum plate thickness gt 250 inch has three grain orientations each with their own strength values.

The software determines the smallest rectangle bounding box that aligns with the grain direction to fit the flat pattern. Once the crystallites are elongated they appear as the grain that we see in cold rolled steel. The long tranverse lt the short transverse st and the longitudinal l. From mil hdbk 5 7075 t62 2 501 3 000 thick stock ultimate tension allowable stress is l 67 ksi lt 70 ksi and st 66 ksi.

When sheetmetal is bend perpendicular to rolling direction grain rearranges. During sheet metal processing rolling operation material grains are arranged in the direction of rolling. That has negligible impact on part strength. A plate s grains run parallel to the rolling direction.

Bending with the grain gives a different result than bending against it.